Power Form 35
 
 
Standard Characteristics Powerform 35/35p
Construction
10mm-40mm 35xk7(16xK7:6xK7+6xK7-1x7)
42mm-60mm 35xK19S(16xK19S:6xK19s+6x
K19S+6xK19s-6xK195-1x19S)
Compacted
Yes No
   
Tensile Grade N/mm
1960 2160
   
Finish
Bright Galvanished
   
Lay Direction
Right hand Left hand
   
Lay Type
Ordinary Langs
   
Average Fill Factor (0%)
74.5
Turn value at 20% of breaking force degree/rope lay
0.2
Nominal rope lay length (NRD=Nominal Rope Dia.)
5.8x NRD
Discard Criteria
Refar to ISO 4309:1990
 
 
Nom. Rope
Dia. Mm
Approx Dia
ins
Approx Mass
kg/100m
MINIMUM BREAKING FORCE
 
 
 
GALVANISED & UNGALVANISED
 
 
 
ROPE GRADE
 
 
 
1960 N/mm*mm
2160 N/mm*mm
 
 
 
kN
tonnes
kN
tonnes
10
 
51.4
90.2
9.2
98.6
10.1
11
7.0/16
61.7
109
11.2
119
12.1
12
 
72.9
131
13.4
141
14.4
13
½
84.6
155
15.8
167
17
14
 
97.1
180
18.4
192
19.6
15
 
114
206
21
221
22.5
16
5.0/08
130
233
23.8
252
25.7
17
 
140
261
26.6
285
29.1
18
 
159
300
30.6
321
32.7
19
3.0/4
178
331
33.8
358
36.5
20
 
197
372
37.9
399
40.7
21
13/16
222
402
41
434
44.3
22
7.0/08
240
444
45.3
484
49.4
23
 
261
482
49.2
528
53.8
24
15/16
286
531
54.2
2572
58.3
25
 
312
575
58.6
623
63.5
26
1
340
621
63.3
661
67.4
27
 
356
665
67.8
722
73.6
28
 
391
720
73.4
788
80.4
29
1.1/8
425
769
78.4
833
84.9
30
 
445
827
84.3
904
92.2
32
1.1/4
505
944
96.3
1035
105
34
 
574
1065
108
1156
118
35
1.3/8
602
1125
114
1216
124
36
 
644
1185
121
1286
131
38
1.1/2
712
1326
135
1437
146
40
 
807
1477
150
1588
161
42
1.5/8
884
1485
151
 
 
44
 
961
1618
165
 
 
46
 
1060
1765
180
 
 
48
1.7/8
1150
1935
197
 
 
50
 
1230
2078
212
 
 
52
 
1360
2256
230
 
 
54
 
1450
2417
246
 
 
56
 
1560
2610
266
 
 
58
 
1680
2788
284
 
 
60
2.3/8
1800
2958
301
 
 
 
 
a
 
Features
1) Powerform 35/35p has the highest of all low rotation hoist ropes
2) A sample of rope from each production batch is tested to destruction in order to confirm compliance with catalogue breaking force values
3) Maximum resistance to rotation
4) Suitable single part and multi-part hoist reeving systems
5) H for use onigh fatigue life resulting from the unique copaction process
6) Increased resistance to crushing. Recommended for multi layer spooling operations
7) Increased abrasion resistance resulting from the unique compaction process
8) Optional plastic impregation, (P) signifies full plastic impegnation of the Steel Core
9) Fully lubricated in manufacture